Creality Hyper PLA Filament - 1.75mm 1kg Grey

26-00029071
3301010340
Grey
CompanyCreality Part Number3301010340
In Stock
Ships in 24 Hours
2990
Gropbotronics Store Availability
Availability in Retail Store
Payments & Shipping

10x Faster Printing
Thanks to the high fluidity and fast cooling formula, Hyper Series PLA supports up to 600mm/s print speed. High fluidity provides sufficient melting and extrusion, while rapid cooling provides fast shaping for high-speed printing.

High Precision
High stability ensures small changes in thermal expansion and cold contraction even when printing at high speeds, bringing high precision in dimensions and better results.

Higher Toughness
With higher tensile strength than ABS and higher toughness than traditional PLA, Hyper Series PLA brings better structural bearing capacity to the printed models.

Uniform Wire Diameter, Stable Extrusion
Based on two-way laser diameter measurement, the filament diameter accuracy is 1.75±0.03mm, which makes it flow out more smoothly.

Neat Winding with Smooth Printing
Precise filament diameter control and automatic winding arrangement are combined to ensure smoother printing without tangling.

  • Basic Data:
    • Filament Typ: PLA
    • Diameter: 1.75mm
    • Tolerance: 0.03mm
    • Weight: 1.00kg
    • Lenght: 333m
  • Printing Parameter:
    • Recomended Printing Temp Min: 190ºC
    • Recomended Printing Temp Max: 230ºC
    • Recomended Printbed Temperature Min: 25ºC
    • Recomended Printbed Temperature Max: 60ºC
    • Recomended Printing Speed Min: 30mm/s
    • Recommended Printing Speed Max: 600mm/s
  • General:
    • Specific gravity: 1.25
  • Elongation
    • Elongation at break: 6.304 %
  • Flexural:
    • Flexural Strenght: 92.381 %
    • Flexural Modulus: 2490.178
  • Other
    • Impact Strenght Unnotched: 8.8344 KJ/m2

Warranty
Δεν καλύπτεται με εγγύση απο τον Κατασκευαστή
Company
Creality
G. Weight
1.4kg
Color
 Grey
Diameter
1.75 mm
Roundness
≥ 95 %
Printing Temperature
190-230 °C
Tolerance
±0.03 mm
Reel
  • 1 kg