eSUN ePLA-LW 1.75mm 1kg – Black

Κωδικός:

16-00017584

Part Number: ePLA-LW-P175B1

Απόχρωση:

Μαύρο

ΚατασκευαστήςeSUN Part NumberePLA-LW-P175B1

Διαθέσιμο

Αποστολή σε 24 ώρες

€39⁹⁰

+ −

Κάνε μια ερώτηση

Διαθεσιμότητα Καταστημάτων

Πληρωμή & Μεταφορικά

Προβολη ολων των παραλλαγών ως λίστα

Column filling

Ταξινόμηση Τιμή	Ταξινόμηση Διαθεσιμότητα	Ταξινόμηση Κωδικός	Ταξινόμηση Απόχρωση
€39⁹⁰	Διαθέσιμο + − ΑΓΟΡΑ	16-00017584	Απόχρωση: Μαύρο

Περιγραφή
Χαρακτηριστικά

Light weight pla filament is a material specially developed for aeromodelling. The interlayer bonding is stable, and the foaming rate and strength can be controlled by adjusting the printing temperature. ePLA-LW uses active foaming technology to achieve lightweight, low-density PLA parts, the foaming volume ratio is 220%, and the density is as low as 0.54g/cm3.

Foaming makes the layered pattern almost invisible, and the surface of the printed item is matte and delicate. Under the same model and at the same speed, the Lightweight PLA filament enables the model aircraft to have a lighter wing load and a lower stall speed, which can greatly improve the performance of the model aircraft.

Specifications

Density as low as 0.54g/cm3
Foaming volume ratio 220%
Free adjustment of strength and foaming ratio
Excellent matte surface effect
Good interlayer adhesion
Easy to paint
Excellent printability

Notes

The first layer speed setting is consistent with the actual printing speed, set to 100% of the actual printing speed, turn off the first layer and small area printing speed reduction function, the first layer extrusion rate is consistent with the actual foaming extrusion rate, such as 270 degrees set to 45% of the first layer extrusion rate; if the bed adhesion is too strong, you can set the bottom valve when printing.
Pay attention to the maximum operating temperature of the printer. Most Teflon tube printers cannot be operated for a long time above 250℃. Long-term printing above this temperature may cause blocking. If the temperature exceeds 250℃, high temperature printers are required for printing.
Yellowing of printed parts after high temperature foaming is a normal phenomenon. Lowering the printing temperature can minimize it.
Since the ePLA-LW foams continuously in the melting cavity of the high-temperature nozzle, the retraction basically does not work. Stringing is normal during printing. It is recommended to print the rc plane in vase mode to reduce the effect of stringing.
Foaming ratio is related to temperature, printing speed, nozzle melting cavity size, pay attention to compare model design wall thickness according to your own printing situation, adjust extrusion rate, temperature, speed and other parameters.

Filament Properties Table

3D PRINTING FILAMENT	ePLA-LW
Density(g/cm3)	1.2
Heat Distortion Temp(℃,0.45MPa)	53
Melt Flow Index(g/10min)	8.1(190℃/2.16kg)
Tensile Strength(MPa)	32.2
Elongation at Break(%)	68.9
Flexural Strength(MPa)	41.31
Flexural Modulus(MPa)	1701
IZOD Impact Strength(kJ/㎡)	8.58
Durability	4/10
Printability	9/10
Extruder Temperature(℃)	190 – 270℃
Bed temperature(℃)	45 – 60°C
Fan Speed	100%
Printing Speed	40 – 100mm/s
Heated Bed	Optional
Recommended Build Surfaces	Masking paper, PVP solid glue, PEI