High temperature nylon reinforced with 15% carbon fiber
Carbon fiber reinforced
Heat resistant
Low sensitivity to moisture
Excellent wear resistance

Intelligent fiber-reinforced technology: The Smart Fiber-Reinforced Technology significantly improves the mechanical properties and heat resistance of the material and relieves the internal stresses during the printing process through the fibre fabric structure, which leads to good dimensional stability of the printed part and no warpage.

Low sensitivity to moisture: aeCarbon Ultra PA-CF is based on modified high-temperature nylon, the saturated moisture absorption rate of which is only a tenth of ordinary PA6, thus eliminating the deficiencies in the mechanical properties and dimensional stability of nylon materials, which change greatly after being absorbed by moisture.

Super abrasion resistance: aeCarbon Ultra PA-CF has a low coefficient of friction, self-lubricating properties and excellent wear resistance, which can easily meet all types of high-strength gears or industrial applications with high wear requirements.

Suggestions

Since carbon material places high demands on the material and heating capacity of the nozzle, the following nozzles are recommended for use: hardened steel nozzles, ruby nozzles. It is also recommended that the thickness of the heating block be longer than 12mm.
Please put the unused filament back in the original bag made of aluminium foil for sealed storage in order to preserve the quality of the material.
The filament can be dried in an oven at 80-100 ° C for 4-6 hours to restore the print quality.
After printing is complete, the printed part can be annealed to further improve strength.

Technical data

Diameter	1.75 mm
Density	1.15 g/cm³
Water absorption	0.6%
Melting temperature	231°C
Melt index	10.78
Tensile strength(X-Y) Young's modulus(X-Y) Elongation at break (X-Y)	121.77 ± 4.28 MPa 7807.99 517.99 MPa 1.88 ± 0.11%
Bending strength (X-Y) Bending modulus (X-Y)	190.85 ± 2.07 MPa 8512.22 ± 241.31 MPa
Charpy impact strength (X-Y)	7.74 ± 1.13 KJ/m²

Recommended printing conditions

Nozzle temperature	300-320°C
Recommended nozzle diameter	0.4-1.0 mm
Recommended build surface treatment	PEI Film or Coating with PVP glue
Build plate temperature	70-80°C
Raft separation distance	0.08-0.12 mm
Cooling fan speed	Off
Print speed	30-120 mm/s
Retraction distance	3-6 mm
Retraction speed	1800-3600 mm/min